電工鋼硅鋼片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan

電工鋼硅鋼片2 供貨形式6.2.1 產(chǎn)品以卷供貨，簡(jiǎn)稱(chēng)鋼卷。鋼卷的重量應(yīng)符合訂貨要求，卷重一般3～10 噸，特殊卷重應(yīng)在訂貨時(shí)協(xié)商并在合同中注明。6.2.2 鋼卷通常以切邊狀態(tài)交貨。用戶(hù)有特殊要求時(shí)，應(yīng)在訂貨時(shí)協(xié)商并在合同中注明。6.2.3 鋼卷內(nèi)徑應(yīng)在 500mm～520mm 范圍內(nèi)，鋼卷內(nèi)徑為 508mm。6.2.4 鋼卷應(yīng)由同一寬度的鋼帶連續(xù)、遼寧遼陽(yáng)附近緊密卷繞，卷的側(cè)面應(yīng)盡量平直，自重下不塌卷。6.3 交貨狀態(tài)鋼帶以終退火并兩面涂敷絕緣涂層的狀態(tài)交貨。6.4 表面質(zhì)量6.4.1 鋼帶表面應(yīng)光滑清潔，無(wú)油脂，無(wú)銹漬，無(wú)影響使用的缺陷。6.4.2 鋼帶表面允許存在不影響材料正常使用的在厚度偏差允許范圍內(nèi)的基板缺欠、遼寧遼陽(yáng)本地絕緣涂層缺欠，如輕微劃傷、遼寧遼陽(yáng)本地色差、遼寧遼陽(yáng)本地輥印、遼寧遼陽(yáng)本地斑紋等缺欠。