電工鋼硅鋼片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

電工鋼硅鋼片當磁極化強度隨時間按正弦規(guī)律變化，其峰值為某一標定值，變化頻率為某一標定頻率時，單位長度電工鋼片（帶）沿磁化方向上發(fā)生磁致伸縮所引起的表面振動聲壓水平為 A 計權磁致伸縮速度水平。3.5 表面絕緣電阻 surface insulation resistance在規(guī)定條件下所測得的直流電阻，即產品在加直流電壓，經過一定時間極化過程后，流過帶鋼（片）表面的泄漏電流對應的電阻，其符號為 C，單位為Ω·mm2/面或Ω·cm2/面。3.6 層間電阻 inter-lamination resistance產品疊片間，即上、青海海北本地下兩個表面的絕緣電阻，稱為層間電阻，其符號為 RA，理論上是表面絕緣電阻的 2 倍，單位為Ω·mm2/片或Ω·cm2/片。4 分類本文件的材料的等級是根據(jù)磁極化強度在1.7T、青海海北本地頻率在50Hz下的 比總損耗名義值P1.7/50(W/kg)、青海海北材料公稱厚度進行牌號分類，并按產品特性和特殊用途，細分為普通型、青海海北高磁極化強度型、青海海北磁疇細化型、青海海北耐熱磁疇細化型、青海海北低噪聲型、青海海北配電變壓器專用型、青海海北特高壓變壓器專用型、青海海北無涂層型八類。